热处理对TC21钛合金中厚板组织性能的影响
董震键，王勤波，陈海涛，王小翔，庞洪
（宝鸡钛业股份有限公司，陕西宝鸡721014）
0 材室温强度达到最高值，且塑性较高；时效温度为590C×4h/AC时，板材室温强度及塑性较固溶后有所提高；板
材选用900℃×1h/AC+590℃×4h/AC固溶时效热处理，可以得到室温强度及塑性的良好匹配关键词：TC21钛合金；热处理温度；显微组织；力学性能
中图分类号：TG146.2*3；TC113.25
文献标识码：A
Influence of HeatTreatmentontheMicrostructureand
Propertiesof TC21TitaniumAlloyPlates
DONG Zhen-jian, WANG Qin-bo, CHEN Hai-tao, WANG Xiao-xiang, PANG Hong(Baoji Titanium Industry Co.,Ltd.,Baoji,Shaanxi, 721014, P.R. China)
Abstract: Different heat treatment on the microstructure and properties of TC21 alloy plates is studied. The results show that the solution temperature at 900 °C, plat strength reaches the highest value and higher plasticeity at room temperature; when aging temperature is at 590 °C × 4h/AC, the plate strength at room temperature and the plasticity after solid solution both increase; when the plate ages at 900 °C × 1h/AC +590 C × 4h/AC solid solution for the heat treatment, a good match of the strength at room temperature and ductility can be achieved.
Key words: TC21 titanium alloy; heat treatment temperature; microstructure; mechanical properties
0前言
TC21钛合金是我国自主研发的高强高韧钛合金，合金名义成分为Ti-6AL-3Mo-2Nb-2Zr= 2Sn-1Cr，经简单固溶处理后，其抗拉强度可以达到 1100MPa以上.该合金与美国的Ti-62222S强度相当，因其优异的综合性能，已在国内宇航领域获得大量使用
在国外Ti-62222S钛合金作为比Ti-6AL： 4V合金更高强度和可靠性的材料，被制成锻件、棒材、厚板、薄板等产品，作为大截面飞机机身构件在 F-22飞机上获得使用.由于TC21合金强度高，加工难度大，前期国内主要以锻造方式生产棒材和锻件.对于TC21合金锻造产品已进行大量试验研究工作，而对于中厚板材尚未有过相关研究，为此应对
收稿日期：2015~0527
TC21中厚板材进行相关研究.本文针对TC21中厚板进行了热处理对其性能及组织影响的初步研究，为后期板材批量化工业生产给予技术参考
试验方案 1
试验采用三次真空自耗电弧熔炼的3T铸锭，在3150T锻造机上多火次锻造为150mm×500mm x1000mm的板坏，用金相法测得该合金相转变温度为955±5℃.板坏经过1200mm四辑可逆式热轧机在α+β相区两次加热轧制至18mm厚，取样后分别选用六种热处理制度进行研究，确定了TC21 钛合金的最佳固溶温度；在选定的固溶温度基础上进行4次时效热处理实验，来确定最佳的时效热处理温度.本次实验试样采用水切割方式，在PH-12-12环保型节能高精度箱式电阻炉进行热处理后，
作者简介：董震键（1979-），男，2000年毕业于洛阳有色金属职工大学压力加工专业，工程师，