第31卷第1期 2010年2月
·材料研究·
热处理技术与装备
RECHULIJISHUYUZHUANGBEI
激光熔覆与热喷涂镍基合金涂层
的微观组织和性能
冯旭东
（河南理工大学材料科学与工程学院河南焦作454000）
Vol.31,No.1 Feb,2010
摘要：利用热喷涂和激光熔覆技术分别制备了镍基涂层，采用显微组织和显微硬度法对两种涂层进行了对比研究。结果表明：两种工艺得到的涂层组织基本相同，主要包括-Ni固溶体、硼化物、碳化物+镍-固溶体共晶以及合金渗碳体等全属间化合物，热喷涂涂层组织中未形成共晶体；两种涂
层的平均硬度均高于基体，均达到了表面强化的目的。关键词：激光熔覆；热喷涂；镍基合金
中图分类号：TG174.444文献标识码：B
文章编号：1673-4971(2010)01-0028-04
Microstructure and Properties of Ni-based Alloy Coating
by Laser Clading and Thermal Spraying
FENG Xu-dong
(College of Materials Engineering,Henan Polytechnic University, Jiaozuo Henan 454003,China) Abstract : The properties of two kinds of Ni6O coatings which are deposited by laser cladding and thermal spraying respectively are studied by microstructure and micro-hardness. The results show that the costings formed by both processes have same micrsatructure which mainly composed of y-Ni solid solution, eutectic of boride, carbide + y-solid solution and intermetallic compounds such as cementite alloys etc. The eu-tectics are not formed in the thermal sprayed coating. The average micro-hardness in coatings are higher
than that of the matrix and have been achieved the purpose of surface hardening Key words: laser cladding; thermal spraying; Ni-based alloys
0引言
热喷涂是利用热源将喷涂材料加热熔化，并利用热源自身的动力将熔化的喷涂材料雾化，然后喷涂到工件表面形成涂层的一种工艺。本试验使用的热源为氧-乙炔火焰。热喷涂技术自上世纪四五十年代以来，在我国不断发展，目前已广泛应用于航天及民用工业中。但是，该工艺存在一定的不足之处，如涂层成形过程易形成气孔和夹杂，主要是由于热源提供的能量密度不足，不能使粒子充分熔化造成
收稿日期：20090928
的。为了解决此问题，多年来，国内外学者们一直在寻求一种喷涂后的重熔处理工艺，如激光重熔等，以此来减少喷涂的质量缺陷，取得了良好的效果]。
激光熔覆是利用高能量密度的激光束，对工件很薄的表层及涂层进行熔覆处理。当激光束扫描后，熔覆的表面合金由于基体材料的迅速导热而产生极高的冷却速度而快速凝固结晶。不但产生牢固、良好的冶金结合，即结合强度高，而且还获得细小均匀的显微组织，即涂层微观组织优良，从而获得具有非常优