第32卷第5期 2011年10月
热处理技术与装备
RECHULIJISHUYUZHUANCBEI
Vol. 32,No.5 Oet,2011
·工艺研究·
金属磁记忆技术用于去应力退火评估的可行性研究
罗龙清，瀚伟，于润桥，王少军
（南昌航空大学测试与光电工程学院，江西南昌330063）
摘要：本文基于磁致仲缩效应的新型金属磁记忆无损检测技术，利用金属磁记忆信号与应力大小严格的对应关系，对金属磁记忆检测技术用于去应力退火进行评估，进行可行性研究。通过研究分析发现，金属磁记忆信号与45钢的去应力退火程度有一致的单调性，通过检测金属磁记忆信号磁场
的强度，可实现对去应力退火工艺的评估。关键词：金属磁记忆；去应力火；评估
中图分类号：TG441.8文献标识码：A
文章编号：1673-4971(2011)05-0017-03
TheProbabilityResearchofEvaluatingtoStressRelieving
Annealing With the MMM Technology
LUOLong-qing，JUWei,YuRun-qiao,WANGShao-jun
(School of Measuring and Optical Engineering, Nanchang Hongkong University Nanchang Jiangxi 330063, China)
Abstract: Base on the new MMM technology with magnetostriction effect,the MMM technology probability evaluating to stress relieving annealing is studied by the relation between the MMM signal and the stress. Our experiment shows that the relation between MMM signal and the steel 45 residual stress has the similar monotonicity, and verified the reality that evaluate the level of stress relieving by testing the MMM signal. Key words:metal magnetic memory ; stress relieving annealing;evaluate
一般情况下，铸件、锻件、焊接件、经冷冲压等机械加工后的试件存在较大的残余应力。残余内应力的存在会降低尺寸稳定性，导致痒火变形开裂，降低焊缝处金属的承载能力。为了提高试件的机械加工性能和使用性能，往往都要去应力退火。应力消除程度及退火工艺一般通过测量残余应力来评估。测残余内应力的传统方法有应力释放法、X射线法、超声波法和深层应力分布法等，这些传统方法可以很好地测量残余应力。但有一些明显的缺陷，如应力释放法属于有损方法，X射线工艺和操作复杂、成本高，超声波法需要耦合剂等。为此，本文提出用金
属磁记忆检测技术评估退火去应力程度[1]。收稿日期：2011-03-14
20世纪90年代，俄罗斯的杜波夫教授提出金属磁记忆无损检测技术，这种全新的无损检测技术，由于其检测方法简便快捷，至今仍是唯一一种可对铁磁性材料进行早期诊断的无损检测新技术。一经提出，便受到国内外众多学者的高度关注和研究。其原理是铁磁构件在受到工作载荷和地磁场的共同作用下，在应力和变形集中区发生磁致伸缩，使磁组织定向的、不可逆的重新取向[2]。铁磁性材料磁场强度与机械应力（或残余应力)有直接的联系，这种磁机械效应使得铁磁性构件的应力集中区磁场增强，增强的磁信号也就相应的“记忆”了应力集中位置，并且磁场强度随着应力的增大而增强[3-7]。本
作者简介：罗龙清（1985-），男，士，主要研究电磁无损检测技术及仪器。
联系电话：13698418321;Email;luolqing@163.com