粉煤灰轻质混凝土耐腐蚀性特性研究 Research on Corrosion Resistance Characteristics of Lightweight Concrete with Fly Ash
秦炜
（西安铁路职业技术学院，陕西西安710600）
摘要：通过在二氧化硫环境下对两种型号的粉煤灰轻骨料混凝土与普通混凝土在耐腐蚀性性能方面进行对比试验，并借助SEM电镜进行观察腐蚀过程中粉煤灰混凝土微观形态变化的过程，从而揭示粉煤灰是如何提高混凝土的耐腐蚀能力的作用机理，为粉煤灰轻质混凝土的研究和在工程应用提供参考。
关键调：粉煤灰轻质混凝土：二氧化硫；硫化；腐蚀规律
中图分类号：TU528.2
文献标识码：A
文章编号：10058249（2018）04-0048-03 QinWei
(Xi°'An vocational and technical institute, Shan xi, 710600)
Abstract: It is considered that the comparative test of two kinds of lightweight aggregate concrete and ordinary concrete on the corrosion resistance in the sulfur dioxide environment, using SEM to observe the process of the microshape change of fly ash concrete in the process of corosion, so as to reveal the mechanism of improvement on the corrosion resistance of concrete, and provide a reference for the study of lightweight concrete and its application in engineering.
Keywords: fly ash lightweight concrete; dioxide; sulfide; corrosion law
粉煤灰轻骨料混凝土是在普通混凝土的配料基础上掺人一定量的粉煤灰配制而成的。由于混凝土本身并不是无限耐久性材料，大量混凝土建筑面临着被空气中二氧化硫的腐蚀问题，为提高混凝土的耐腐蚀性，我们已经做了一些的研究。本文主要研究了掺加粉煤灰轻骨料的混凝土在二氧化硫的环境下与普通混凝土的耐腐蚀性的对比试验，以及在显微镜下观察分析粉煤灰在混凝土内部作用的微观过程，从而得到粉煤灰耐腐蚀特性研究成果以及其作用机理。
1试验材料及设计 1.1试验目的
本试验采取对比试验的方法，分别对3种不同粉煤灰掺人量的粉煤灰1号混凝土、粉煤灰2号混凝土、普通型混凝土进行对比，记录观测数据并绘制
作者简介：秦炜（1980年～），男，副教授，硕士，研究方向建筑工程。
收稿日期：2018-04-02· 48·
万方数据
曲线图，得出掺加粉煤灰相比于普通型混凝土在耐腐蚀性能方面的影响，在二氧化硫腐蚀过程中，运用SEM电镜对混凝土内部微观形态进行观察与分析，得出粉煤灰作用的机理以及不同粉煤灰混凝土在耐
腐蚀性能的结果。 1.2试验材料
（1）细骨料：经过预试验后，决定选取各项性能指标都合格且粒径小于4mm的中砂。（2）粗骨料：经过预试验后，决定选取各项性能指标都合格且粒径为4mm~25mm的大砂砾。（3）水泥：采用水泥市场上最常见的P·042.5级水泥。（4)水：普通自来水。（5）二氧化硫腐蚀箱用水：采用市场上购买的普通饮用纯净水。
1.3配合比与分组设计
本试验选用了常见的C40混凝土作为基准组。本试件选用最常见的细骨料、水泥和水，以求各种混凝土外加剂以及其余成分的影响降低到最小。
通过查表与反复进行配比试验得到各组混凝土