粉煤灰综合利用
FLY ASH COMPREHENSIVE UTILIZATION
掺粉煤灰水泥胶砂的正交试验研究 Research on Orthogonal Experiment of Cement Mortar Blended Fly Ash
赵鹏，王跃峰，王尉和，赵亚丽，姚彩珍，关博文
（长安大学材料科学与工程学院，陕西西安710054）
2010NO.1
摘要：采用正交试验方法，研究了粉煤灰掺量、细度和Na,SO，掺量对水泥胶砂试块抗折、抗压强度影响规律。结果表明：粉煤灰掺量对水泥胶砂试块的7d抗折、抗压强度影响最显著；粉煤灰掺量和粉煤灰细度对28d抗折、抗压强度影响都比较显著；面Ns,S0，掺量对7、28d抗折、抗压强度影响不大。
关键调：粉煤灰；正交试验；水泥胶砂；抗折强度；抗压强度
中图分类号：TQ177.6*2
文献标识码：A
文章编号：1005-8249(2010)01-0031-03
( Institute of Materials Science and Engineering,Changan University,Xian 710054,China)
Abstract: Using orthogonal experiment,the efects of fly ash content fineness and the content of Na,SO, on folding and compreseive strength(7,28d) of cement mortar are studied. The results sbow that the content of fly ash have the most prominent influence on 7d folding and compressive strength of cement mortar;the content of fly ash and the fineness of fly ash have significant influence on 28d folding and compressive strength of ce-ment mortsr:yet the content of Na,SO, all along have litle influence on 7d,28d folding and compressive strength of cement mortar
Key words fly ash;orthogonal experiment;cement mortar;folding strength;compressive strength
粉煤灰是煤粉经高温燃烧后形成的一种似火山灰质混合材料。本文测试了粉煤灰掺量对水泥凝结时间及安定性的影响；重点研究了粉煤灰掺量、粉煤灰细度、Na,SO，掺量3个因素对水泥胶砂试块7、28d抗折、抗压强度的影响规律。
1试验 1.1
试验原材料
试验原材料包括陕西省某电厂的粉煤灰，
P·C32.5级水泥、Na,SO.、标准砂和自来水。 1.2试验方法
粉煤灰成分见表1。用JXA-8100型电子探针（EPMA)对灰的成分进行分析，用DBT-127型勃氏透气比表面积仪对球磨不同时间的粉煤灰灰比表面积进行测定。测试粉煤灰掺量为0，10%，20%，30%、40%（在胶凝材料体系中的质量分数）水泥的凝结时间及安定性。设计正交试验，试验中选择了粉煤灰掺量、粉
"基金项目：长安大学青年基金
收稿日期：2009-09-14 万方数据
煤灰细度、Na,SO掺量3个因素为变量做水泥胶砂试块，脱模后放在标准恒温恒湿养护箱中（湿度95.0% RH，温度19.5~20.5℃）养护，研究所选的3个因素在因素水平范围内对水泥胶砂试块的7、28d抗折、抗压强度影响规律。
表1
Na,0 0.17
陕西省某电厂粉煤灰的成分
/%
Mgo 0.10
2
结果及讨论
Al,o, 55.86
sio, 35.71
K,o 1.80
Cao 3.35
Fe,0, 3.01
粉煤灰掺量对水泥凝结时间及安定性的影响
2.1
根据《水泥标准稠度用水量、凝结时间、安定性检测方法》（CB/T1346-2001），对掺不同量原灰（未经球磨的灰)的水泥凝结时闻、安定性进行检测，结果见表 2。从表2可看出，随粉煤灰掺量增加水泥的凝结时间变长。与纯水泥相比，粉煤灰掺量为10%、20%时对水泥的凝结时间影响不大；当粉煤灰掺量为30%、 40%时，水泥的凝结时间大幅度变长，可能是由于粉煤灰掺量的增加降低了水泥熟料的浓度，从而降低了交
·31·