粉煤灰综合利用
FLYASHCOMPREHENSIVEUTILIZATION
掺加粉煤灰的污泥沉降浓缩效果与利用
Thickening Property and Utilization of Sewage Sludge Modified by fly ash
苏柳铭，岳蒸飞，陈伟，黄义雄，钱觉时（重庆大学材料科学与工程学院，重庆400045）
2010NO.6
摘要：改善污泥浓缩和脱水性能有利于污泥的处置和利用，从污泥用于建材原材料的角度，试验研究了粉煤灰在污泥沉降浓缩过程中的作用。结果显示，粉煤灰的最佳掺量为5%时，脱水混合物含水率为60%左右，低于纯污泥脱水后80%左右的含水率，将大大有利于后续的处理与利用；经粉煤灰改性后浓缩脱水得到的污泥可用作烧制粒。
关键词：粉煤灰，沉降，浓缩，陶粒
中图分类号：X703
文献标识码：A
文章编号：1005-8249(2010)06-0019-04
SU Liuming, YUE Yan-fei,CHEN Wei, HUANG Yixiong, QIAN Jueshi
(College of Material Science and Engineering, Chongqing University, Chongqing 400045)
Abstract: To improve thickening and dewalering properties of sewage sludge is beneficial to disposal and utilization. The infiuence of fly ash on sludge setlement was investigsted experimentally, It is shown that the moisture content of dewalered sludge with fly ash dosage of 5% was 60%, which is favor for its subeequent proceseing and use, The dewatered sludge modified by fly ash can be used as raw materials to produce ceramsite
Key words:fly ash, setling, thickening, ceamsite
粉煤灰是一种具有潜在活性的粉末状材料，其物
理化学性质取决于燃煤的品种、煤粉的细度、燃烧方式和温度、收集和排灰方法等，其化学成分包括SiOz、 Al,O，和Fe,O，等。粉煤灰比表面积较大，具有一定的吸附能力，其等温吸附规律符合Freundlish吸附等温式，它是一种廉价的吸附材料，有时甚至可代替活性碳、硅胶、活性Al,O，等用作专用吸附剂。
污泥处理主要包括浓缩、消化、脱水等工艺，其目的是降低污泥含水率，减小污泥体积，以减轻后续处理的压力。污泥浓缩方法以重力浓缩应用最为广泛，即污泥在重力场作用下通过自然沉降而分离的方式。污泥重力浓缩后的含水率为95%~97%，还需要进一步降低含水率，可采取压滤、离心等方式将其含水率控制在80%左右。经过浓缩和脱水后的污泥呈"胶状，含水率80%的污泥总体质量比实际固含量多出 4倍，其体积也是干态污泥的4~5倍[2]。降低含水率
*重庆市建设科技项目（城科字2007第38号）和重庆市科技项目
(CSTC2007AB7043）资助收稿日期：2010-10-20 万方数据
只是污泥减容减量的一个环节，最终目标则应是污泥的处理与资源化。污泥建材资源化是污泥利用的重要方向(341，因为污泥的建材资源化不仅利用污泥量大，而且污泥建材生产和使用对环境影响最小[5)。目前多数研究是利用粉煤灰的吸附和分散功能对污水中的有害物质进行吸附沉淀，以达到净化污水的作用，但是仍然会产生大量泥渣，给环境带来负担。直接采用含水率80%左右的污泥与粉煤灰混合烧制建材制品可作为污泥资源化有效途径之一，然面，粉煤灰加入污泥中需要充分混合，烧制后的制品性能才能有所保证，但混合工艺通常比较复杂，而且与高含水率的”胶状”污泥混合比较困难。因此本研究在污泥的最终建材资源化的根本目标下，在污泥的浓缩、脱水阶段掺加粉煤灰，研究其对污泥沉降、脱水性能及排水性质等的影响，同时利用脱水后的混合物烧制陶粒(6-7)，以认识粉煤灰在污泥处理及资源化方面的作用。
1原材料及试验方法 1.1原材料
污泥取自重庆市某污水处理厂的沉淀池，为黑色
·19·