抗泥型低损聚羧酸减水剂的制备与性能研究 Reseach on Preparation and Properties of Polycarboxylate Surperplasticizer for Resistanceclay and Lowslump
骆志超，靳通收，李茜茜，王文彬，陈占虎（河北三楷深发科技股份有限公司，石家庄市051430）
摘要：通过磷酸化异戊烯醇聚氧乙烯醚为大单体和引人乙烯基磺酸钠、丙烯酰胺、丙烯酸、丙烯酸羟丙酯等功能型小单体，在氧化-还原体系下合成了一种具有高含泥量下减水率高、混凝土经时损失小、硬化混凝土强度高、耐久性好的抗泥型低期损聚羧酸减水剂。
关键词：聚羧酸减水剂；抗泥；低损；磷酸化
中图分类号：TU528.042*.2
文献标识码：A
文章编号：10058249(2016)05-0037-04
Luo Zhichao , Jin Tongshou, Li Xixi, Wang Wenbin, Chen Zhanhu
(Hebei Sankai Deeply Developed Technology co., LTD., Shijiazhuang 051430)
Abstract: The resistanceelay and lowslump polycarboxylate superplasticizer (PCE) were synthesized by phosphorylation of the isopentenol polyoxyethylene ether, and introducing vinyl sulfonate acrylamide acrylic acid and hydroxypropyl acrylate in the oxidation=reduetion system. The resuls indicated that the PCE exhibited high water reduction, lowslump and high eompressive strength on the condition of high clay content in concrete.
Key Words; PCE; resistanoeclay ;lowslump; phosphorylation
聚羧酸系高性能减水剂因其具有接量低、减水率高、混凝土落度经时损失小、对混凝土干缩影响小、耐久性好等优点，而在一些高速铁路、高速公路、南水北调、港口码头、水电大坝、市政建设等工程中得到广泛应用1]。但是，在实际应用过程中，近年来由于基建工程量巨增，砂石消耗靠大，优质的砂石资源越来题少，砂石中的含泥量偏高等问题突现。使得聚羧酸减水剂与含泥量高的砂石料适应性差、需水量大、混凝土落度损失快、强度降低等一系列问题函待解决【2-4]。因而，解决含泥土量偏高的砂石料与聚叛酸减水剂的适应性问题，是聚羧酸减水剂能否大量推广使用的一个决定性因素。
*基金项目：石家庄市科学技术局（151160541A），项目名称：抗泥型低垢损聚羧酸系减水剂合成技术的开发
第一作者：路志超(1986~)，男，本科毕业，助理工程师，主要从事混凝土外加剂的研究。
通讯作者：新通收，男，教授，主要从事混凝土外加剂的研究。E-mail;hebeijinduoyanfabu@ 126.com
收稿日期：2016-05-16 万方数据
J.Plank教授研究了聚羧酸减水剂与泥土的作用机理，为抗泥型聚羧酸减水剂的研究奠定了理论基础[5]。目前，市场上有些厂家通过复配缓凝剂或泥土抑制剂来解决这一问题。然面，采用复配还需考虑许多问题，例如，与减水剂相容性差、泌水、凝结时间过长等。基于聚羧酸分子结构的可设计性和可采用单体的多样性，近年来，人们通过分子设计引人具有抗泥功能的单体，如不饱和有机胺、端基含碳-碳双键硅烷、不饱和季铵盐等[6-8]。这类抗泥减水剂对含泥量高的砂石料，在一定程度上能够改善混凝土流动性，但其落度损失仍然较快。因而，抗泥型低损聚羧酸系减水剂的开发备受人们期待。
本文通过磷酸化异戊烯醇聚氧乙烯醚在其分子的长链端引人磷酸基及在聚合物的分子结构中引人功能型乙烯基磺酸钠、丙烯酰胺和丙烯酸羟丙酯短侧链，合成了抗泥型低损聚羧酸减水剂。该减水剂能降低泥土中的高价金属离子对聚羧酸减水剂的吸附，能改善含泥量高骨料配置混凝土的工作性和保性，并具有
· 37 ·