粉煤灰综合利用
FLY ASH COMPREHENSIVEUTILIZATION
2014NO.6
试验与应用
冻融循环过程中混凝土的过冷现象及其原因分析
The Concrete Surfusion and its Cause in Freezing and Thawing Cycle
侯云芬，王玲2，吴越恺'，王振地
（1.北京建筑大学，北京100044；2.中国建筑材料科学研究总院，北京100024）
摘要：在研究冻融循环过程中混凝土和砂浆试件湿度和变形随温度变化规律时发现，在降温段混凝土和砂浆试件以消除过冷现象。试验中采取在砂浆试件中掺人水泥质量1%的碘化银和胆固醇来消除过冷现象，结果表明，掺人碘化银或胆固醇可以使砂浆试件的结冰温度提高5℃左右，即碘化银或胆固醇具有消除过冷现象的作用。
关键词：过冷现象：碘化银：胆固醇；冻融循环：混凝士
中图分类号：TU528.0
文献标识码：A
文章编号：1005-8249(2014)06-0015-04
Hou Yunfen', Wang Ling”, Wu Yuekai', Wang Zhendi?
(1.Beijing University of Civil Engineering and Architecture, Beijing, 100044, China;
2.China Building Materials Academy, Beijing, 100024, China)
Abstract It shows that the freezing point is 15°C, instead of 0'C which is surfusion during freezing and thawing cycle of concrete, By analyzing the cause of surfusion, it concludes that surfusion ean be eliminated by adding condensation nucleus such as silver iodide and cholesterin which can increase the freezing point for 5'C.
Key words; surfusion; silver iodide; cholesterin; freezing and thawing cycle; concrete
耐久性是混凝土的主要技术性能，而抗冻性是耐久性的主要指标之一，也是人们广泛关注的混凝土性能，并且有大量的研究成果。本课题主要研究在冻融循环过程中，随着温度变化混凝土和砂浆的湿度和变形的规律，但是研究时发现，在降温过程中，混凝土和砂浆试件的结冰温度为-15℃左右，而不是水的冰点（为0℃），即存在过冷现象。本文分析了出现过冷现象的原因，并尝试掺人水泥质量1%的碘化银和胆固醇来控制或消除过冷现象。
1原材料与试验设计 1.1原材料
选取普通42.5水泥，性能见表1，标准砂，细度模数为2.6的Ⅱ区中砂，颗粒级配为5min~20min的下钢筋混凝土破坏机理研究（2012CB724602）资助）
收稿日期：2014-09-30 万方数据
碎石。
表1水泥的技术性能
标准稠度用水量/% 29.2
1.2试验设计
凝结时间/min抗压强度/MPa抗折强度/MPa
终凝初凝
211
285
3d 39.6
28d 54.3
3d 5.2
28d 8.1
1.2.1配合比为了控制原材料对结果的影响，研究采用传统配方，即不加掺合料和外加剂，混凝土配合比为水泥：砂：石：水=1：1.84；3.12：0.5，试件为边长 100mm的立方体；砂浆配合比为水泥：标准砂：水= 1：3.8：0.5，试件为边长70.5mm的立方体，砂浆中掺人 1%的胆固醇和碘化银作为过冷度消除剂。
1.2.2试验设计在冻融循环试验过程中同时测定试件的湿度变化，旨在通过湿度变化反映冻融循环过程中的结冰和融化温度。
将湿度数字传感器布置在混凝土和砂浆试件截面形心处（即中心处），为防止试验环境对湿度数据采集的影响，试验中对传感器进行了外加套管的封闭处理，
·15 ·