2014年8月上第43卷第15期
DOI:10. 7672/sgjs2014150063
施工技术
CONSTRUCTION TECHNOLOGY
高强经编聚酯纤维筋增强混凝土梁
抗弯性能试验研究
张季超，霍灵召，许勇，周敏玲，裴海富，张婷婷
（广州大学土木工程学院，广东广州510006)
[摘要】高强经编聚酯纤维筋是一种新型FRP筋。为深人研究高强经编聚酯纤维筋混凝土梁弯曲性能，通过5根高强经编聚酯纤维筋混凝土染和1根钢筋混凝土的弯曲试验，对高强经编聚酯纤维筋混凝土梁正截面抗弯性能进行了广研究。结合试验梁结果，探讨了抗弯承载力计算方法，并与实测值进行了比较，分析了高强经编聚纤维筋增强混凝土梁的裂缝分布形态、最大挠度等特性。
【关键词］混凝土；高强经编聚酯纤维筋；混凝土梁；抗弯强度；挠度；裂缝
［中图分类号］TU377.9
【文献标识码］A
[文章编号］1002-8498（2014)15-0063-04
ExperimentalStudy onFlexuralBehaviorofConcreteBeam Strengthened with StrongWarpKnittingPolyester FiberBars Zhang Jichao,Huo Lingzhao,Xu Yong,Zhou Minling,Pei Haifu,Zhang Tingting
(School of Ciwil Engineering,Guangzhou Unitersity, Guangzhou, Guangdong510006, China)
Abstract:Strong warp knitting polyester fiber bar is a new type of FRP bar. In order to research the bending properties of concrete beam with strong warp kntting polyester fiber bar, five concrete beams reinforced with strong warp knitting polyester fiber bars and one concrete beam reinforced with steel bars were made and investigated in flexure.Based on the experimental study,the calculating method on bending capacity of concrete beams strengthened with strong warp knitting polyester fiber bars was analyzed.The cracks distribution pattern and load-deformation and maximum deflection of concrete beams were analyzed.
Key words: concrete;strong warp knitting polyester fiber bars;beams; bending strength; deflection; cracks
引言 0
钢筋混凝土结构在侵蚀性环境中暴露使用时，钢筋极易锈蚀，降低了钢筋混凝土结构的耐久性，带来极大的安全隐患。高强经编聚酯纤维筋是-种新型纤维增强复合材料（fibrereinforcedplastic
简称FRP），具有抗拉强度高、耐热耐寒性强、化学稳定性好、耐酸碱腐蚀、耐老化、膨胀系数低等优点[2]。高强经编聚酯纤维筋材如图1所示。
目前，国内外对FPR筋混凝土梁正截面抗弯性能已进行较多试验研究。由于FRP筋材料的应*住房和城乡建设部科技计划项目（2013-K4-38）；广东省教育部科学部产学研结合项目（2012B090600046）
[作者简介］张季超，教授，博士生导师，E-mail：zhangjichao1956@ 126.co
【收稿日期］2014-04-29
图1高强经编聚酯纤维筋（涂胶）
Fig.1 Strong warp knitting polyester fiber (gluing）
63
力-应变关系为线弹性，无屈服点等特点，FRP筋梁构件具有较大的裂缝宽度和挠度[。因此，研究 FRP筋梁的挠度和裂缝非常有必要。结合5根高强经编聚酯纤维筋混凝土梁和1根钢筋混凝土梁的弯曲试验结果，探讨了高强经编聚酯纤维筋混凝土梁抗弯承载力计算方法，并与实测值进行了比较；同