O355GNH耐候钢板表面防腐研究
Vol.45No.3 Mar.2015
包胜军，谢昕欣，郭红锋（株洲时代新材料科技股份有限公司，湖南株洲412007）
摘要：以Q355GNH耐候钢板为底材，研究了Q355CNH耐候钢板经镀锌、涂覆防腐涂料、渗锌、达克罗处理后的耐中性盐雾性能。研究表明：经渗锌处理的样板耐盐雾性能较差，经镀锌处理的样板耐盐雾性能取决于镀层膜厚，经达克罗处理、渗锌加达克罗处理及防腐涂料处理的样板耐盐雾性能较好，耐盐雾试验时间均达到6709h。
关键词：耐候钢：镀锌：有机涂层：达克罗：渗锌：盐雾试验
中图分类号：TQ635.2
文献标识码：A
文章编号：0253-4312（2015)03-0069-04
Anticorrosive SurfaceTreatment of WeatheringResistantSteelO355GNH
Bao Shengjun,Xie Xinxin,Guo Hongfeng
(Zhuzhou Times New Material Technology Co.,Lid.,Zhuzhou,Hunan 412007,China)
Abstract:The weathering resistant Q355GNH as the substrate was treated by different methods such as electroplating, anticorrosive organic coating, dacromet, sherardizing and syn ergy thereof to investigate its neutral salt fog resistance. The results showed that the neutral sal fog resistance of the sherardizing sample was not good and the electroplating samplewas subject to the film thickness,whereas,the dacromet sample, sheardizing plus dacromet sample and organic coating sample gave good neutral salt fog resistance up to 6 709 h
KeyWords:Q355GNH; electroplating;organic-coating;dacromet; sherardizing; salt frog test
耐候结构钢是介于普通钢和不锈钢之间的低合金钢，耐候钢板较普通碳钢添加少量铜、镍等耐腐蚀元素，这些元素使钢铁材料在不锈层和基体之间形成一层致密层，阻止了大气中氧和水向钢铁基体渗人，从而提高了钢铁材料的耐大气腐蚀能力。耐候钢具有强韧、塑延性好、易成型、可焊割、耐磨蚀、耐高温、抗疲劳等特性，其耐候性为普通碳钢的2~8倍，涂装性为普通碳钢的1.5~10倍，主要用于铁道、车辆、桥梁、塔架等。Q355NH耐候钢是焊接耐候钢，其执行标准为GB/T4171-2008，其厚度为6~40mm，宽度为1800~2800mm，长度不限）。Q355GNH中除Fe 和微量杂质外的其他化学成分见表1。
表1Q355GNH耐候钢中的其他化学成分 Table1ChemicalcompositionofQ355GNH
其他成分
c si Mn p S Cu Cr Ni
作者简介：包胜军（1972一），男，高级工程师，研究方向为桥梁支座及高建列车系统产品表面处理技术。
%/at ≤0.12 0.2~0.75 ≤1.0 0.07~0.15 ≤0.02 0.250.55 0.3~1.25 ≤0.65