特种PVC抗石击耐磨蚀防腐涂料
Vol. 43No. 7 Jul,2013
糜万俊，阔大清，徐小云（江苏华奥高科技发展有限公司，江苏仪征211400）
摘要：以聚氟乙烯树脂为主体的特种无溶剂涂料，可防止车辆在行进中砂石等破坏性材料对车辆身板底板、轮罩及车身的撞击和损坏，并起减震、隔热、密封作用，同时涂膜具有柔韧性、弹性、耐冲击性、耐磨蚀及防腐性能
关键词：PVC涂料：高温固化：车辆减震：隔热：密封
文章编号：0253-4312(2013)07006804
中图分类号：TQ633.5*2
文献标识码：A
PvC Chip Resistant Corrosion Protective Coatings
Mi Wanjun,Kan Daqing,XuXiaoyun
(Jiangsu Huaao Technology Derelopmen Co. ,Lid. ,Yizheng, Jiangsu 211400,China)
Abstract: A special solvent free chip resistant coatings with polyvinyl chloride resin(PVC) as binder was developed, to prevent the damage of wheel hubs,bottom plates and ve-hicle body due to impact and hit of stone chips during running, and provided shock absorp-tion, heat insulation and sealing effects. The coating film showed characteristics of good flexi-bility, elasticity, impact resistance, abrasion resistance and corrosion resistance.
Key Words:PVC coating;high temperature curing ;vehicle shock absorbing;heat insulation;sealing
特种PVC抗石击耐磨蚀防腐涂料是喷涂在车辆底部的一种保护性涂料，作用是防止车辆在行进中砂石等破环性材料对车辆身板底板、轮罩及车身的撞击和损坏，并起减震、隔热、密封作用。涂膜对金属底材有很好的附着力，且涂膜的耐冲击性、柔韧性、耐擦伤性及与车身的结合配套性等优异。
本研究制备的特种PVC抗石击耐磨蚀防腐涂料
不但能应用于普通车辆，面且能在海军两栖作战妞克上进行涂装，防止两栖作战坦克在行进中砂石等材料对底板、轮罩及车身的破坏，并能长期耐海水腐蚀
1
实验部分 1.1原料
邻苯二甲酸二辛酯（DOP）、稳定剂（三盐）：工业级，金陵石化；增粘剂（Euretek505）：原Ciba公司：聚
氯乙烯树脂（C65V、E5/65C）：工业级，德国Vinnolit 公司；金红石型二氧化钛、脱水剂（CaO）：自制：纳米活性碳酸钙（SPT）：工业级，英国ICI公司：气相二氧
化硅：工业级，扬州昊能化工有限公司。 1.2涂料的制备
涂料基本配方见表1。
在捏合机中加入DOP，开始搅拌，搅拌速度为 300r/min，依次加人稳定剂、聚氟乙烯树脂、增粘剂脱水剂、金红石型二氧化钛、SPT、触变剂。充分搅拌均匀，研磨，过滤，出料。
2产品标准、涂膜性能及测试方法 2.1产品标准及实测物理化学性能
该产品目前没有国家标准，本研究采用意大利标
作者简介：康万假（1968—），男，高工，主要从事防扇材料、两烯酸树脂等的研究 68