基于SBS改性沥青特征指标的多次再生评价
邹桂莲，鄂然，张陈
(华南理工大学土木与交通学院.广东广州510641)
摘要：为更好地对回收的SBS改性沥青路面材料进行循环利用，采用延度、弹性恢复率、黏度、黏韧性等特征性指标对改性沥青多次老化再生效果进行评价。结果表明：随着老化与再生次数增多，各指标对老化与再生的敏感性不同，延度、韧性指标最敏感；多次老化再生的效果逐渐变差，典型的流变特性逐渐丧失，建议对SBS改性沥青进行3次以上再生时，可考虑将之作为老化的普通沥青使用。
关键词：SBS改性沥青；多次再生；效果评价；特征指标
中图分类号：U414.03
文献标志码：B
Evaluation of Effect of Repeated Recyclingon
PropertiesofSBSModifiedAsphalt ZOU Gui-lian, YAN Ran, ZHANG Chen
(Sehool of Civil Engineering and Transportation, South China University of Technology,
Guangzhou 510641 , Guangdong, China)
Abstract: In order to better recycle SBS modified asphalt pavement materials, the effects of repeated aging and recycling on the modified asphalt were evaluated by the characteristic indices such as ductility, elastic recovery rate, viscosity and tenacity. The results show that with the increase of the times of aging and recycling, the sensitivity of each index differs, and the ductility and tenacity were the most sensitive; the effect of repeated recycling gradually deteriorates, and the typical rheological properties are gradually lost, It is recommended that SBS asphalt which
has been recycled for more than three times should be regarded as ordinary aged asphalt. Key words: SBS modified asphalt; repeated recycling; effect evaluation; characteristic index
引言 0
目前，国内首批大规模使用SBS改性沥青铺筑的沥青路面已经使用超过20年，2000年后大量铺筑的SBS改性沥青路面也已使用十几年，这些路面已经进人大修、重建阶段，这将产生大量的废旧SBS 改性沥青路面材料。为更好地对材料进行循环利用，研究SBS改性沥青的再生及多次再生机理与效果具有重要意义-1}。
国外对SBS改性沥青再生机理与效果开展了大量的研究4"，但是结论并不统一，有研究认为老收稿日期：2017-03-04
基金项目：国家科技支撑课题项目（2014BAC07B01）
化过程使得SBS改性剂明显降解，再生并不能恢复改性沥青的特有性质，再生SBS改性沥青混合料抗疲劳能力较差；也有研究认为，通过对老化SBS改性沥青进行再生试验，发现老化SBS改性沥青性能得到恢复，SBS改性沥青再生是可行的。国内的一些学者与道路工作者也相继开展了SBS改性沥青及其混合料的再生性与机理研究"12}，有学者认为通过恰当的方式可以实现SBS改性沥青的完全再生；也有研究认为再生剂对SBS改性沥青的再生效果不佳，再生SBS改性沥青的耐久性与低温性能较差=13-17]。本文采用针人度、延度、弹性恢复率、黏度、