复合材料层合板挖补修复工艺研究
刘诗琪1,2
杨涛2杜宇2
（1天津市现代机电装备技术重点实验室，天津300387）
（2天津工业大学机械工程学院，天津300387）
文摘针对不同挖补斜度的复合材料层合板使用韧性胶黏剂Araldite"2015，对修补后的试件使用弯曲和拉伸性能进行评价。结果表明；铺层方式为±45°]4层合板在弯曲载荷作用下修补后修补效率最高能达到 119.6%，拉伸载荷作用下修补效率最高能达到71.4%；铺层方式为[0°/90°]层合板在弯曲载荷作用下修补后修补效率最高能达到82.1%。结果可为实际修补提供依据和指导。
关键词复合材料，挖补修补，韧性胶黏剂
中图分类号：TB32
D0I:10.12044/j.issn.10072330.2017.02.016
RepairingTechnologyofLaminatedCompositePatch
LIU Shiqi'2
YANG Tao',2
DUYu?
(1 Advanced Mechatronics Equipment Technology Tianjin Area Major Laboratory, Tianjin 300387)
(2 School of Mechanical Engineering, Tianjin Polytechnic University, Tianjin 300387)
aa eaa Araldite 2015. The repaired specimens using bending mechanical properties and tensile mechanical properties were evaluated. The results show that the overlay [±45°], laminates under bending load repair efficiency can reach the highest of 119. 6% , under tensile load repair efficiency can reach the highest of 71.4% ; layer [0°/90°]4, laminates under bending load repair efficiency can reach the highest of 82. 1%. These resuits can provide the basis and guid-ancefor the actual repair.
Key wordsComposite laminates,Strap repair,Ductile adhesive
0引言
复合材料具有比强度和比模量高、可设计性强、疲劳性能好、耐腐蚀等许多优异性能！]，近年来已经越来越多的在民用和军用领域大量应用。伴随着越来越多的使用，复合材料出现损伤的几率也大大增加。为了不影响后续的使用以及经济性方面的考虑，复合材料的修补已成为一个受到广泛关注的问题。对于这些损伤，在一些承力不大的部位，可以忽略不予修补，但是对于一些重要部位，大面积更换部件又不经济划算[2]，对原有复合材料构件进行修补便成为一种经济可行的方案。
修补大致分为机械连接修补和胶接修补。机械收稿日期：2016-12-11
基金项目：国家自然科学基金（11372220）
连接修补因其需要在原结构上开孔而会引起不必要的应力集中，较少地被应用于实际修补中。而胶接修补能够很大程度上减小应力集中，结构增重小，能最大程度保持气动外形抗腐蚀，并且工艺流程简洁快速而越来越多的来代替机械连接修补(3)。
胶接修补主要分为贴补法和挖补法[4]。贴补法和挖补法的主要区别在于是否对原损伤孔进行重新打磨。贴补法是在原损伤部位上直接粘贴上与原材料相同的补片，而挖补法则是在原损伤结构上进行打磨后补以相同材料的补片进行粘接修补。
胶接修补在工艺上应考虑纤维铺层、修补角度、胶黏剂选择等多个因素(3)。国内外在胶接修补方面
第一作者简介：刘诗琪，1991年出生，硕士研究生，研究方向为复合材料成型技术与装备。E-mail;972775799@qq-com 通信作者：杨涛，教授。Email；yangtao@tipu.edu，cn
字航材料工艺万方数据
http://www.yhclgy.com
2017年第2期
- 71 -