乙烯-醋酸乙烯-氟乙烯共聚树脂合成试验研究
刘松涛'，缪晖
（上海氯碱化工股份有限公司，上海200241）
[关键调］乙烯；醋酸乙烯；氯乙烯；共聚；溶胀，分散剂
[摘要］介绍了在10L聚合釜中合成乙烯醋酸乙烯-氧乙烯（EVA-g-VC)共案树脂的试验情况。分别研究了EVA种类及用量、EVA的溶胀方法、助剂对聚合过程和树脂颗粒性能的影响规律，制得的EVA-g-VC共聚树脂的加工性能基本达到了国外同类产品水平。
[中图分类号］TQ325.3;TQ325.5［文截标志码］A［文章编号］1009-7937(2011)09-0013-06
Experimental study on the synthesis of vinyl/ vinyl acetate/ vinyl chloride copolymer resin
LIUSongtao,MIAOHui
(Shanghai Chlor-Alkali Chemical Industry Co.,Ltd., Shanghai 200241, China) Key words: vinyl; vinyl acetate; vinyl chloride; copolymerization; swelling; disperser
Abstract: Experiments on the synthesis of vinyl/ vinyl acetate/ vinyl chloride ( EVA-g-VC) copolymer resin in 10 L polymerizer were introduced. Influences of types and dosages of EVA, swelling method of EVA and additives on the polymerization process and performances of resin par ticles were investigated. The processing properties of EVA-g-VC copolymer resin obtained could reach the level of foreign products.
笔者研究了EVA种类及用量、EVA溶胀方法、
性能优良的大宗共聚树脂，在世界氯乙烯共聚树脂中，其产量仅次于氯乙烯一醋酸乙烯共聚树脂，居第 2位[1-2}。经过30多年的发展，EVA-g-VC共聚树脂生产工艺日益成熟，品种也逐渐增多，使用该树脂生产的产品具有更加广泛的综合性能，应用领域逐步扩大。它广泛应用于医用制品、薄膜、片材、高级电缆、鞋底、硬质抗冲建材、发泡制品、涂料、黏合剂等，而且是聚氯乙烯硬制品和软制品的良好抗冲和增韧改性剂。近几年来，国外在化学改性聚氯乙烯方面开展了大量的工作。国内浙江化工研究院、江苏金浦北方氯碱化工有限公司和浙江大学也先后开展了EVA-g-VC共聚树脂的开发工作，但由于EVA 原料问题，并未工业化生产[3]。因此，该树脂的生产在国内还是空白，加工厂家所需EVA-g-VC共聚树脂基本依赖进口。如河南瑞贝卡集团公司为亚洲最大的假发生产厂家，每年需进口日本钟渊公司生产的EVA-g-VC共聚树脂约350t。
［收稿日期］2011-0302
分散剂和引发剂等助剂对聚合过程和树脂颗粒性能的影响规律，本文中将介绍在10L聚合釜中研制
EVA-g-VC共聚树脂的情况。 1试验部分
1.1主要设备与仪器
CONF-10-4型10L聚合釜，北京化工研究院；J-W1微型柱塞计量泵，杭州之江石化设备有限公司；2XZ一1型旋片式真空泵，临海市谭氏真空设备有限公司；RB20-110自动恒温热水泵，上海爱思杰制泵有限公司；SS-Ⅱ三足式离心机，张家港龙泰机械公司；BrobenderPL2000-6转矩流变仪，美国Thermo公司；MastersizerMs20激光粒
径测试分析仪，英国Malvern公司。 1.2主要原料
氯乙烯，上海氯碱化工股份有限公司；有机过氧
[作者简介］刘松涛（1977-），男，硕士，工程师，2008年毕业于上海交通大学化学化工学院，主要从事氯乙烯聚合和新
产品开发工作。