第45卷第11期
2017年11月【材料与性能】
聚氯乙烯 Polyvinyl Chloride
硫酸钙晶须/PVC硬质复合材料性能的研究
王寿元·
（云南正邦科技有限公司，云南昆明650224）
【关键调】PVC;硫酸钙晶须；复合材料；性能
Vol.45,No.11 Nov.，2017
【摘要】采用双辑混炼-模压成型的方法制备了硫酸钙晶须/PVC硬质复合材料，研究了硫酸钙晶须用量对复合材料性能的影响。结果表明：随着硫酸钙晶须用量的增加，试样拉伸强度、弯曲强度逐渐下降，冲击强度、热变形温度先升后降，弯曲弹性模量和维卡软化温度呈升高趋势，且热稳定性明显提高。
[中图分类号】TQ325.3
【文献标志码】B【文章编号】1009-7937(2017)11-0019-04
Studyonpropertiesofcalciumsulfatewhisker/PvCrigidcomposites
WANG Shouyuan
(Yunnan Zhengbang Technology Co.,Ltd.,Kunming 650224,China)
Key words:PVC; calcium sulfate whisker; composite; property
Abstract: Calcium sulfate whisker/PVC rigid composites were prepared by twin-roll mixing and compression molding.The effects of calcium sulfate whisker amount on the properties of the composites were studied. The results showed that with the increase of calcium sulfate whisker amount, the tensile strength and flexural strength of the composites decreased gradually, the impact strength and thermal de-composition temperature first rose and then decreased, the flexural modulus and Vicat softening tempera-ture increased, and the thermal stability was improved obviously
硫酸钙晶须（CalciumSulfateWhisker，缩写为 CSW）是一种长径比大、强度高、刚度高、白度高、热稳定性好的纤维状单晶体，且其价格远低于其他高性能填料，因此将CSW作为聚合物复合材料的增强填料得到研究人员的重视[1-5]。目前，CSW在增强聚丙烯（PP）、PA-66、酚醛树脂等案合物复合材料中的应用较为成功[*-*]。但是，由于CSW与聚合物基体间的界面相容性差，导致亲水晶须和疏水聚合物基体之间的负载转移差，晶须易从聚合物基体中拉出，复合材料的增强效果有限【"]。
PVC是一种重要的高分子材料，具有良好的物理性能、化学性能，且价格低廉。以PVC树脂为基体的复合材料种类较多，如PVC木塑复合材料【10-11]、秸秆粉/PVC复合材料[12]、石墨烯/PVC 复合材料")和晶须/PVC复合材料（如钛酸钾晶
·【收稿日期】2017-08-18
须(14]）等。然而，CSW在PVC复合材料中的应用较少[u5-]。
笔者以CSW为增强填料，通过混炼、模压制得 CSW/PVC硬质复合材料，研究了CSW用量的变化对复合材料力学性能、耐热性能、颜色等的影响。
1试验部分 1.1主要原料
CSW：长径比1：（100~200），直径20~30 μm，白度90%，pH值5~8，云南力达一矿物技术有限公司；稳定剂，SMS318，百尔罗赫塑料添加剂（江苏)有限公司;PVC-SG5树脂，云南省能源投资集团有限公司；PE蜡，6102，科莱恩化工（中国）有限公司；硬脂酸，SA1801，印尼斯文有限公司。
【作者简介】王寿元（1970一），男，1997年毕业于武汉工程大学，现任云南正邦科技有限公司董事长，主要从事氯碱、
600
19
万方数据