第39卷第7期
2011年7月【科研与生产】
聚氯乙烯 Polyvinyl Chloride
Vol.39,No.7 Jul.，2011
105m3聚合釜聚合中途注低温水PVC生产工艺
吴彬，尹建平
（新天业（集团)有限公司天展化工公司，新疆石河子832000）
[关键词］PVC;聚合签;聚合中途注水；聚合配方
[摘要］介绍了案合中途注低温水工艺在105m’聚合釜PVC生产中的应用情况，运行情况表明：中途注低温水工艺对PVC产品质量没有影响，SG5型PVC树脂聚合反应时间可缩短近50min，提高了聚合釜的生产能力。
［中图分类号］TQ325.3
［文献标志码］B［文章编号］1009-7937(2011)07-0005-05
Process of adding low-temperature water during polymerization
forproduction of PvCin 105 mpolymerizer
WU Bin,YIN Jianping
(Tianchcn Chemical Industry Co.,Xinjiang Tianye（Group)Co.,Ltd.,Shihezi 832000,China)
Key words: PVC; polymerizcr; adding water during polymerization; polymcrization formula Abstract: Thc application situations of process of adding low-tempcraturc watcr during poly-
mcrization for production of PVC in 1o5 m’ polymcrizcrs wcrc introduced. The rcults showcd that the process of adding low-temperature water during polymerization had no influcnccs on qualitics of PVC products, thc polymcrization timc for PVC-SG5 rcsin could be shortened by 50 minutes, and thus the production capacity of polymerizers wcre incrcascd.
Foundation item: kcy scicntific and tcchnological program of Xinjiang Production and Con-structionCorps(2010GG11)
在悬浮聚合PVC生产过程中，环境温度过高会影响聚合釜的换热效果，使反应过程不易控制，聚合釜生产能力大幅度下降，并存在一定的安全隐患，给PVC 生产企业带来很大生产压力。PVC树脂的生产工艺早已成熟，尤其是聚合工艺，经过近几十年的发展更趋完善。聚合反应是在单体和去离子水的液相体系中进行的，随着转化率的增加，聚合液相体系的体积缩小，黏度增大，气相空间也增大；聚合体系黏度增大，则搅拌功率升高，聚合并粒的概率增大，同时导致传热能力下降，会造成体系反应温度不均匀，使单釜产量、产品质量下降1-2)。传统工艺中，聚合中途注水工艺用水为常温(20～25℃)水，存在用水量大、能耗高、效率低等问题。同时由于新疆地处西北地区，夏季环境温度可达到40℃以上，直接导致聚合釜的换热能力下降，制约了生产能力的提高。为了降低聚合釜的换热负荷，同
［收稿日期］201103-11
时提高聚合转化率和生产过程的稳定性，缩短聚合反应时间、生产周期并增加产量，新疆天业(集团)有限公司天辰化工公司（以下简称天辰化工）尝试在105m 聚合釜PVC生产过程中采用中途注低温水工艺。
中途注低温水工艺简介
天辰化工采用105m内夹套全流通聚合釜生产PVC。在聚合工序中途注水管线中间增设1台换热器，对原来中途注的常温水进行换热降温，使其温度降至设定温度再注入聚合釜中，在注水量不变的前提下，低温水的注入可以降低釜温，有效缓解聚合釜的换热压力，使换热效率大大提高，聚合釜的签温、釜压控制更加容易，对聚合釜的反应过程控制更为有利，并可提高生产效率。
[基金项目］新疆生产建设兵团重点科技攻关计划（2010GG11)
[作者简介］吴彬(1970一)，女，博士，高级工程师，2010年毕业于北京理工大学，现任新疆天业（集团)有限公司常务
副总经理。