第45卷第5期
2017年5月【安全与环保】
聚氰乙烯 Polyvinyl Chloride
氯化氨气体含冷凝酸导致检测过氟案例分析
曹国玉，，张军峰，邦小艳，杨伏东，高琦，高树丽（陕西北元化工集图有限公司，陕西榆林719319）
【关键调】VCM；氯化氢气体；冷凝酸；过氯案例
Vol.45,No.5 May，2017
【摘要】介绍了氯化氢及VCM合成工艺流程，阐述了VCM合成用氯化氢气体因冬天气温低两含有少量冷疑酸，在分析检验过程中检测出含有游离氢而被追手动操作停车。针对此间题，提出了整改方案，优化了控制指标，制定了防范措施，取得了显著成效。
【中图分类号】TQ325.3
【文献标志码】B
[文章编号］10097937(2017)05004303
Case analysis of detected excessive chlorine due to condensation acid contained in hydrogen chloride gas
CAO Guoyu,ZHANG Junfeng, GUO Xiaoyan,YANC Fudong,GAO Qi, GAO Shuli
(Shaanxi Beiyuan Chemical Industry Co., Ltd., Yulin 719319, China)
Key words: VCM; hydrogen chloride gas; condensation acid; excessive chlorine case
Abstract: The synthesis process of hydrogen chloride and VCM was introduced. The hydrogen chloride gas used as raw material for VCM synthesis contained a few condensation acids because of che low temperature in winter. Thus free chlorine was detected in the process of analysis and test, which led to forced manually stop. In order to solve the problem, improving plans were proposed, control index was optimized, and preventive measures were made, so remarkable results were achieved.
在电石法PVC生产过程中，常见的安全事故是 VCM合成工段氟化氢含有的游离氧与乙炔发生剧烈反应，发生爆炸燃烧，损坏设备设施，危及人员安全。发生过氯事故的原因诸多，主要是氟化氢合成过程中，氯气和氢气的配比控制不好或压力不稳，氧气和氢气调节阀失灵造成氧化氢气体含有少量游离氯。游离氟的存在会给安全生产带来极大的危害，此类事故易发、额发，给装置的安全生产和稳定运行造成很大的威胁。目前预防过氯的主要保护逻辑有乙炔大阀与预热器、混合器的温度或温度梯度联锁，当温度或温度变化率超过设定值时，乙炔大阀自动关闭，同时氮气阀打开充氮气，防止形成负压，使空气进入系统。
2015年12月，陕西北元化工集团有限公司（以下简称北元化工）VCM合成工序因连续检测出氯
【9【
化氢含游离氟而被迫停车2次，停车后调取数据曲线时，发现混合器和预热器温度未发生变化，同时氧碱中控分析也未检测出游离氯。针对这一问题，北元化工展开认真调查和事故分析，最后确定为冷凝酸含有游离氧所致，分析氯化氢时冷凝酸进人气量管致使检测溶液发生变色，造成误判。随后提出整
改方案，制定了防范措施。 1工艺流程
1.1氯化氢合成工艺
氢气来自氢处理工序，通过氢气管道上的各个手动和自动阀送至石墨合成炉，氯气和氢气在炉内混合燃烧生成氯化氢气体，反应热由夹套中的纯水冷却后带走，再经过炉顶冷却器，使氯化氢气体温度降至45℃以下后进人氟化氢缓冲罐，经缓冲后进人
【作者简介】曹国玉（1983-），男，助理工程师，2008年毕业于柏林学院化学工程与工艺专业，2008年3月参加工作，
曾参与100万Va聚氯乙烯项目施工管理和组织系统开车调试工作，现从事生产总调度工作。
43