文摘通过对QJ3074一1998中的测试原理和测试夹具的改进，提高了四探针法线材电阻率测试仅的测试精度并拓宽了测试范围，获得了试验验证。通过试样长度对测试结果的影响及试验条件对测试结果的影响等试验，系统评价表征了各种碳纤维的电阻率，为建立碳纤维电阻率测试方法标准奠定了重要的技术和数据基础。
关键词碳纤维，电阻率，测试方法，评价方法
Evaluation and Characterization on Electric Resistivity of Carbon Fiber
Chen Conghui'
Sun Yinjie
HeFengmei'
Li Jianping?
Zhang Zhenglong
(1National Key Defense Laboratory of Advanced Functional Composite Materials Technology, Aerospace Research Institute of Materials & Processing Technology,Beijing100076)
(2Beijing Aerospace Institute for Measuring and Testing,Beijing100076)
AbstractBy improving testing principle and testing tongs in QJ3074-—1998,,the testing accuracy of four probe method for electric resistivity of wire materials was raised and the testing scope was widened. Through the experiments of the effect of sample length and testing conditions on the testing results ,the electric resistivity of various carbon fibers is characterized systematically and that laid an important technical foundation for establishing standard of the testing method of electric resistivity for carbon fibers.
Key wordsCarbon fiber,Electric resistivity,Testing method,Evaluating method
1引育
碳纤维具有高比强度、高比模量、耐高温及导电等优异性能，在航天、航空、兵器、船舶、核等国防领域具有重要作用。
碳纤维的电阻率与其成分、石墨化程度、缺陷等相关，表现为半导体的特征，低温主要受杂质的控制，高温表现为电子电导)的特性。其电阻率测试方法，在文献[2~5]中有报道，常用的测试方法为电压电流法和电桥法，前者分双探针法和四探针法，后者分单电桥法和双电桥法，四探针法和双电桥法均可以消除接触电阻和引线电阻的影响，适宜低电阻测试， GB/T3048.2—94规定电阻小于10Q应采用四探针法或双电桥法。本文采用四探针法。
航天科工防御技术研究实验中心制订了 QJ3074—1998《碳纤维及其复合材料电阻率测试方法》，但该标准为定长测试模式，不能表征碳纤维电阻
86006060
率随长度变化，且未涉及试样状态（如带胶和未带胶），环境温度的影确等。本文对碳纤维的电阻率测试方法
进行了研究，并对不同型号碳纤维进行了表征。 2测试方法的改进
QJ3074-1998的测试原理见图1。
图1双操针法测试原理
Fig.1Testing model of Q13074—98
1~直流电源;2电流表：3一电压表；4试样;5—可变电阻