模压石英/酚醛复合材料的力学和热物理性能
李云宽丁仁兴于棘（航天材料及工艺研究所，北京100076）
文摘采用力学、热物理等测试方法，研究模压成型石英/酚醛复合材料制品性能，并与模压成型高硅氧/酚醛复合材料制品进行了对比分析。结果表明，模压石英/酚醛复合材料具有较好的力学性能，而且其线胀系数是模压高硅氧/酚醛复合材料的一半，在中低值、较低热流、较长烧蚀时间条件下具有很小的热变形。
关键词石英纤维，酚醛，模压
ThermalandMechanicalPropertiesofMouldedQuartzPhenolicComposites
DingRenxing
LiYunkuan
YuMiao
（AerospaceResearch InstituteofMaterials&ProcessingTechnology，Beijing100076）
AbstractThe properties of moulded quartz phenolic composites are studied by the methods of mechanical and physical tests, comparing with moulded high silica phenolic composites. The result shows that moulded quartz phenolic composite not only has good mechanical property,but also has much more lower thermal deformation in the environ-ment of low enthalpy,low heat flux and long-time ablation as the property of half linear expansion coefficient compa-ring with moulded high silica phenolic composite.
Key wordsQuartz fiber, Phenolic,Moulded
0引言
以树脂为基体的玻璃纤维增强复合材料具有比强度高和比模量高、可塑性好、独特的设计性等优良特性，在航空航天、军工等诸多领域应用广泛)。模压制品是玻璃纤维增强酚醛树脂复合材料中的一种。酚醛树脂具有良好的力学和耐热性能，尤其具有突出的耐瞬时高温烧蚀性能。玻璃纤维作为复合材料中的广泛应用的增强材料，具有耐高温、耐腐蚀、强度高、绝热性及绝缘性好的特点。
新型航天飞行器对防隔热材料提出了中低焙值、较低热流、烧蚀时间较长（≥300s）的防隔热要求，传统的瞬时防热用树脂基防热材料如高硅氧/酚醛等在长时间烧蚀环境下存在烧蚀变形问题，影响飞行器气动外形及防热层的防隔热效果。本文研究了模压成型石英/酚醛复合材料制品性能，并与模压成型高硅
氧/酚醛复合材料制品性能进行了对比分析。 1实验
收稿日期：2013-05-08
1.1材料
酚醛树脂，河北高碑店市铜山化工厂生产；短切石英纤维，湖北菲利华石英玻璃股份有限公司；短切高硅氧纤维，陕西华特玻璃纤维有限公司；溶剂，工业酒精。
1.2试样制备
按配比制作短切石英纤维/酚醛树脂预混料，装人平板模具中模压成型。平板试验件脱模后按相应标准加工性能测试试样（密度、拉伸、线胀系数、热导率、比热容等），其中小发动机烧蚀试样尺寸为190 mm×120mm×20mm，电弧风洞烧蚀试样尺寸为260
mmx260mm×20mm。 1.3性能测试
分别测试模压成型石英/酚醛复合材料密度（GB/T1463—2005）、拉伸强度（DqES77—98）、断裂延伸率（DqES77—98）、线胀系数（GJB332A—2004）、热导率（GB/T10295—2008）、比热容（GJB330A—
作者简介：李云宽，1987年出生，助理工程师，主要从事防热材料方面的研究。E-mail：liyunkuan2008@163.com
宇航材料工艺http：//www.yhelgy.com2013年第4期万方数据
49-