·新材料新工艺·
新型改性氰酸酯及其复合材料性能
英杨智勇
王磊林娜潘玲英
（航天材料及工艺研究所，北京100076）
文摘采用新型催化剂、增初剂制得了一种改性氰酸酯树脂，对新型改性氧酸酯树脂的工艺性、耐热性、力学性能进行了评价，并对其复合材料的介电、力学性能进行了研究。结果表明新型改性氧酸酯树脂具有良好的工艺性，适合热熔法制备预浸料；树脂及其复合材料的力学及介电性能优良，可在180℃下使用，适合高性能透波材料和高频电路板使用。
关键词树脂基复合材料，氟酸酯树脂，力学性能，介电性能
PerformanceofANewTypeofCyanateEsterResinandCompositeMaterials
Pan Lingying
LinNa
WangLei
YangZhiyong
( Aerospace Research Institute of Materials & Processing Technology ,Beijing100076)
AbstractThe processing,heat-resistance and mechanical properties of novel modified cyanate ester ware evalu-ated in this article, The dielectric property and mechanical properties of cyanate ester matrix composite materials were also studied. The results showed that the cyanate ester adapted to madding prepreg by hot-melt methods because. of its good process. All of the cyanate ester and composite materials had nice mechanical properties and could be used under 180°C, The composite materials are suitable for use as for high performance microwave-transparence materials and high frequency circuit boards.
Key wordsResin matrix composites, Cyanate ester resin,Mechnical property,Dielectric property
0
引言
氰酸酯(CE)复合材料具有优良的力学、耐热及耐湿热性能、耐空间环境性，且在很宽的温度（-160 ~220℃）和频率范围（10*~10"Hz）内具有稳定且极低的e(2.8~3.2)和tan8(0.002~0.006)，成为高性能天线罩及空间结构的首选材料(1-3]。目前国外已经商品化的CE透波材料品种有BASF公司的 5575-2、ICIFiberite公司的X54-2、Hexcel公司的 HX1584-3、Dow化学公司的XU-71787等(4-5)。国内对氰酸酯树脂的研究起步较晚，研究对象主要是双酚A型氰酸酯树脂体系，由于氰酸酯树脂在热催化下易发生自聚合反应，目前国内商品化的氰酸酯树脂预没料制备多采用溶剂法，该方法生产成本高、产品性能分散性大，污染环境、效率较低。同时用溶剂法制备预浸料会将挥发份引人复合材料体系中，不利于材料的固化成型和提高材料的综合性能(6)。
本文对一种采用新型催化剂、增韧剂制得的改性
氰酸酯树脂体系工艺性、耐热性、力学性能进行了研究，并对其复合材料的力学性能及介电性能进行了全面评价，以评价新型改性氰酸酯复合材料在高性能结构-透波一体化复合材料构件上应用的可能性。
1实验 1.1原料
改性氰酸酯树脂及热熔预浸料，自制。预浸料增强体为QW220C-90a石英纤维织物，南京玻璃钢研究院生产。
浇注体试样制备
1.2
把树脂置于120℃烘箱预热60min，然后倒人模具于125℃的真空烘箱中抽除气泡，按以下制度固
化：120℃/1h→+160℃/1h→190℃/4h。 1.3复合材料试样制备
将QW220/氰酸酯预浸料按所需的厚度放人热压罐中模具内固化，具体固化工艺为：120℃/1h-→ 160℃/1h→190℃/4h。
收稿日期：2012-05-12
作者简介：王磊，1980年出生，博士，高级工程师，主要从事树脂基复合材料方面的研究工作。E-mail;didiwind1980@163.con
宇航材料工艺http://www.yhclgy.com2012年第4期万方数据
45