低温容器3.5Ni钢的焊接
尹伟'，周珍珍？，张庆素
（中国石油天然气第七建设公司，山东青岛266300：
2.机械科学研究院哈尔滨焊接研究所黑龙江哈尔滨150028）
摘要：采用氢弧焊和埋强焊的方法焊接了3.5Ni钢板材，研究了不同焊接工艺参数对3.5Ni钢-101℃冲击韧性影响，通过试验掌握3.5Ni钢的焊接和材料性能，提出了最佳的焊接工艺参数，为3.5Ni钢低温容器设备的制造提供了可靠的质量保障。
关健调：3.5Ni钢；焊接材料；冲击韧性中图分类号：TC444
3.5Ni steelweldingof cryogenicvessels
Yin Wei',Zhou Zhenzhen’,Zhang Qingsu?
(1. China National Petroleum Seventh Construction Company,Qingdao 266300,
China ;2 . Harbin Welding Institute, China Academy of Machinery Science&Technology,Harbin 150028, China) Abstract: 3. 5Ni steel plates were welded by argon arc welding and submerged are welding, and the effect of different welding parameters on impact toughness( 101C )of 3.5Ni steel plate was researched. The properties of welding and materials were grasped and the optimum welding parameters were put forward by experiment,
which providing reliable quality guarantee for cryogenic vessel facility of 3.5Ni steel. Key words: 3. 5Ni steel;welding material; impact toughness
0前言
随着石油化工和煤化工的发展，对低温设备的需求越来越多，掌握低温钢材的焊接技术及其制造技术是关键。3.5Ni钢是含Ni系列钢材的一种，其中最低使用温度要求满足在-101℃下的各项性能，其技术难点在于如何解决3.5Ni钢焊接接头的低温冲击韧性问题。低温容器不仅要求钢材具有良好的性能，而且要求通过焊接、热处理后焊接接头也要保证低温使用要求，因此对焊接材料的选择和焊接工艺的制定要求较高，研究在于掌握焊接最佳工艺和焊接材料的选择，从面解决实际产品焊
282016年第4期万方数据
接工程中遇到的低温冲击不足问题。
1母材3.5Ni钢和焊材的性能指标
3.5Ni钢板材的强度和冲击韧性都不存在问题，主要关键问题是焊接接头的冲击性能，为此焊接材料的选择采用国产优质焊材，哈焊所威尔公司生产的氩弧焊材料HS06Mn35DR和埋弧焊材料H06Mn35DR/ SJ208DR。板材的成分及性能主要依据ASTMA203E 的相关规定，焊接材料的成分及性能主要依据AWS A5.23、AWSA5.28和NB/T47018—2011标准的规定，其中焊接的低温冲击性能由原来的-101℃时大于等