【摘要】力学性能是混凝土的重要性能，其中又以强度最为重委，它通常可以反映混凝土质量的全说，混凝土的强度越高，其孔腺率就趋低，混凝土的抗渗性得列提高，图两其各方面耐久性得到改善，磨细石灰石粉是具有一定化学反应性的矿物掺合料，可改善混凝土的工作性，使混凝土易于择和与浇筑成型，混凝土的施工质量容易得到保证，
[Abstract ]Mechanical properties is an importantperfomance ofoncrete,and the strength isthe most important factor,and itcan usually reflectthe whole picture ofthe quality ofconcrete.The higher the strength ofconcrete, the lower porosity, and the permeability resistance of concrete is improved, so the durability of the various aspects will also be improved. Ground limestone is mineral admixtures of a certain chemicalreaction,it can improvethe workability ofconcrete,easymixingand pouringthe concretefoming,constructionqualityofconcrete easilybeguaranteed.
【关键调】混设土；大温差；力学性能
[Keywords Jconcrete; the largetemperature difference; mechanical propertie
【中图分类号】TU528.041
【文献标志码]A
[DO1l10.13616/j.cnki.gcjsysj.2015.07.040
1引言
迄今为止，石灰石粉矿物掺合料在水泥水化中作用的研究还较少，认识也不一致，几乎未见石灰石粉用于高性能混凝土的研究，而渣和钛矿渣等的研究利用也很少。磨细石灰石粉是具有一定化学反应性的矿物掺合料，它具有很多优良的特性。石灰石粉光滑的球形颖粒可以改善混凝士的工作性，使混凝土易于拌和与浇筑成型，混凝土的施工质量容易得到保证。石灰石粉还可以降低混凝土的水化温升，这对大体积混凝土、大坝混凝土是非带有利的。此外，细分散的碳酸钙颗粒对 C,S的水化有明显的晶核效应，可加速C,S的水化，提高混凝
【项目基金】河北省交通运输厅科学技术计划项目：干燥大温差地区混凝土质量超前预报和控制研究（012010343）
【作者简介】张嘉微(1980~)，女，河北沽源人，工程师，从事公路工
程管理研究，（电子信箱）736089088@qq.com。万方数据
【文章编号】1007-9467(2015)07-0145-03
土的早期强度。以下就石粉掺量、胶凝材料数量、石粉细度以及引气剂等因素对混凝土抗压和抗折强度的影响进行研究讨论，并探讨其机理。各组试验所用石灰石粉的比表面积均为
899m/kg，未作特殊说明时，胶凝材料总量为580kg/m。 2石粉掺量对混凝土力学性能的影响
本组试验通过改变石粉掺量研究其对混凝土抗压、抗折强度的影响(见图1、图2)。石粉取代水泥量分别为5%、10% 20%、30%。研究表明，40%的中砂砂率对超高强混凝土的流动性和强度来说是最佳砂率目，本课题研究主要采用了这一砂率。试验配合比见表1。
表1单掺石灰石粉的混凝土配合比
编号 J DI D2 D3 D4
胶凝材料/kg/m）水泥
石粉
580 551 522 464 406
· 20 116 174
水胶比 0.23 0.23 0.23 0.23 0.23
砂率 40 40
减水剂 0.9 0.9 0.9 0.8
珊落度(mm 167 206 215 240 230 145