2014年3月第45卷第2期
燃料与化工 Fuel & Chemical Processes
炼焦煤焦化特性评价指标探讨
鲍俊芳薛改凤詹立志陈鹏
（武汉钢铁（集团）公司研究院湖北省炼焦煤利用重点实验室，武汉430080。
5
摘要：介绍了奥亚膨胀度、基氏流动度、罗加指数、胶质层指数、黏结指数和镜质组平均最大反射率等冶金煤焦化特性评价指标的建立和测试方法，以及各评价指标在我国的应用情况。同时讨论了各个指标对胶质体的原生黏结
性、膨胀程度引起的黏着性和焦炭残留物强度这3个焦化特性的表征。关键词：炼焦煤；焦化特性；评价指标
中图分类号：TQ520.1
文献标识码：A
文章编号：10013709（2014）02000504
Evaluation index of coking characteristics of coking coal
Bao JunfangXue GaifengZhan LizhiChen Peng
( Research Institute Wuhan Iron & Steel Co -, Ltd., Hubei Key Laboratory of Coking , Wuhan 430080 , China
Abstract: This paper introduces the establishment and test method of the evaluation indexes of metal -lurgical coal coking characteristics such as Audibert -Arnu dilatation, Gieseler fluidity,Roga index, plastic layer index , caking index and average maximum reflectance of vitrinite ,and the application of the evaluation indexes in China. The characterization of each index to primary caking property of plas -tic mass , adhesivity and coke residual strength caused by expansion is also discussed in this paper . Key words: Coking coal ; Coking characteristic ; Evaluation index
煤由多种有机化合物混杂而成，由于成煤年代、
原始植物以及成煤环境条件不同，不同煤在外在表征、理化性质和工艺性质上都有很大的差别。人类对炼焦煤焦化特性评价指标的建立集中在20世纪 20~40年代。19世纪末至20世纪初，为制取高强度焦炭以满足炼铁生产需要，英、法、德等国家致力于炼焦煤焦化特性的基础研究，并将显微镜引人煤的岩相组分和变质程度研究，取得了丰硕的研究成果。研究发现炼焦煤作为制取高强度焦炭的原料，其变质程度、黏结性、膨胀性和热塑性是煤焦转化机制的关键因素，并创立了相应的评价方法。本文介绍了炼焦煤焦化特性的几种评价指标并对其进行探讨。
炼焦煤焦化特性评价指标的建立及应用 1
1.1奥亚膨胀度
1926一1929年法国奥迪贝特研究创立了煤的奥亚膨胀度（6值，%），1933年阿努对其改进，现在西欧各国广泛采用”。奥亚膨胀度的测试要点是收稿日期：2013-05-27
作者简介：鲍俊芳（1972-），女，教授级高级工程师
将煤样打击压实制成一定规格的煤笔，置人标准口径的膨胀管内，按规定升温加热，压在煤笔上的压料记录煤样在管内的体积变化，以体积曲线膨胀上升的最大距离占煤笔原始长度的百分数，表示煤的膨胀度6值的大小。
在国际分类中，奥亚膨胀度与葛金焦型并列作为冶金煤划分亚组的分类指标。我国1985年以国标GB5450一85发布.并与Y值并列作为我国煤炭现行分类中区分肥煤的指标。国内焦化企业应用该指标较少，宝钢利用6值指导配煤和预测焦炭强度2]，武钢使用6值鉴定具有高膨胀、低流动特殊性质的印尼、莫桑比克等进口煤的煤质，避免不合理使
用对焦炭质量造成不利影响。 1.2胶质层指数
1932年前苏联列姆萨保什尼可夫和列帕巴齐列维奇建立了胶质层指数测定方法‘3]。此法模拟工业焦炉炭化室，通过对特制煤杯中的煤样单侧加热，使其形成一系列的等温层面，并使煤杯中煤样