总第263期 2017年第11期
河北冶金 HEBEI METALLURGY
转炉炼钢中用石灰石
部分代替石灰的生产实践
王玉刚，樊赛，陈东宁，刘道孟，赵广勋（河钢集团邯钢公司一炼钢厂，河北邯郸056015）
Total No.263 2017,Numberl1
关键词：从理论上分析了氧气转炉用石灰石部分代替石灰造渣炼钢的可行性。根据物料平衡与热平衡，进行了广工业冶炼试验。试验结果表明：氧气转炉使用石灰石部分代替石灰冶炼所生产的钢水能够满足所需的终点成分要求：同时还能减少环境污染与资源浪费，降低炼钢辅料成本约4.36元/t，可为企业带
来可观的经济效益，具有很好的推广价值。关键词：转炉炼钢；石灰石；石灰；碱度；成本
中图分类号：TF713.3
文献标识码：A
doi: 10. 13630/j. cnki. 13 1172. 2017. 1114
文章编号：10065008(2017)11005404
PRODUCTIONPRACTICEOFPARTIALLIMESTONE INSTEADOFLIMEINCONVERTERSTEELMAKING WangYugang,FanSai,Chen Dongning,LiuDaomeng,Zhao Guangxun(No.1 Steel Mill of HBIS Group Hansteel Company,Handan,Hebei,056015)
Abstract: The feasibility of partial limestone used for oxygen converter instead of lime was analyzed in theory. According to the material balance and heat balance, the industrial smelting test was carried out. Experimental results show that the liquid steel produced by partial limestone instead of lime can meet the requirements of end point components, reduce environmental pollution and resources waste, reduce the acces-
sories cost about 4. 36 yuan/t, bring considerable economic benefits, and has good popularization value. Key Words : converter steelmaking; limestone; lime; alkalinity; cost
引言
0
“氧气转炉用石灰石代替石灰造渣炼钢”的方法已经在实验室中进行了长期的研究，用这一方法，将石灰石直接加入转炉中，在炉内烧成石灰做造渣剂，减少石灰运输、装卸和输送的机械损耗，取消石灰石烧设备，减少炉外熳烧环节和能量浪费。充分利用了转炉的余热，减少了大量的粉尘和CO 的排放，保护了环境，同时获得大量煤气。既节省了成本，又创造了资源。在当前环保压力下，石灰的生产受到了严重制约，造成石灰的供应紧张。为了缓解石灰供应间题，河钢邮钢一炼钢厂用部分石灰石代替石灰进行冶炼实践。根据转炉炼钢热平衡计算，利用
收稿日期；2017-07-25
作者简介：王玉刚（1984－），男，助理工程师，2013年毕业于河北联合大学冶金工程专业，现在河钢集团邯钢公司一炼钢厂工作，E-mail :361904470@ q- com
54
万方数据
石灰石代替部分石灰及冷料达到转炉热平衡。
使用石灰右代替右灰的理论依据
1
（1）满足转炉冶炼时间
石灰石受高温分解方程式：
CaCO;→CaO+CO2
(1)
AGcaco,=169120144.6T J/mol
在900℃左右，石灰石就会受热分解，而氧枪开吹时转炉内铁水温度一般在1300～1400℃之间，转炉熔池火点温度可达到1600℃以上，因此，炉内温度远高于石灰石的分解温度。石灰石人炉后，立即由表及里急剧升温，促使石灰石表面碳酸钙的分解激烈进行。有资料表明"原本在炉外需要熳烧3～5h的石灰石在转炉炉内由于内外表面巨大的温差，便右灰右搬烧速度加快，搬烧时间降到5 min以内，这个时间不影响转炉生产节奏。转炉内石灰石随温度的分解如图1所示[】