总第180期 2011年6月
文章编号：10099700(2011)030021-04
南方金属 SOUTHERNMETALS
Sum.180
高频燃烧炉红外吸收法测定铁矿石中的硫含量
武映梅，戴清明，彭娟
（广东省韶关钢铁集团有限公司，广东韶关512123）
摘要：介绍利用高频燃烧炉红外光谱法对铁矿石中不同含量的硫进行测定，通过对助熔剂及用量、样品称量、样品与助熔剂加入顺序的选择，分析时间与比较水平的选择等试验，确定了方法的最佳分析参数.该法方便快捷，分析结果令人满意，测定范围在0.008%~20%，精密度0.64%~3.12%（视样品硫含量）.该方法符合铁矿石国家标准
《GB6730.16、GB6730.17》的测试要求. 关键调：铁矿石；硫；红外吸收法
中图分类号：0657.33
文献标识码：B
Determinationofsulfurinironorebyinfraredabsorptionspectrometrywith
highfrequencyinductionfurnacecombustion
WU Ying-mei, DAI Qing-ming, PENG Juan
(Shaoguan Iron and Steel Group Co. ,Lad.,Shaoguan 512123,Guangdong)
Abstract : The method of determining sulfur content in iron ore by infrared absorption spectrometry with high frequency in duction furmace combustion is described in the article, The optimal test parameters for the determination were selected based on the type and dosage of flux,weight of sample,sequence of adding the sample and flux, as well as on the selections of test time and comparison level, Being convenient and quick,the method can yield satisfactory results with a determination range of 0. 008 ~ 20%, and a precision of 0. 64 ~ 3. 12%depending on the sulfur content of the sample. The method is also in
accordance with the National Standards for Iron Ore "CB 6730. 16,CB 6730. 17", Key words : iron ores; sulfur; infrared absorption spectrometry
0前言
铁矿石是钢铁工业高炉冶炼生铁的主要原料，硫在钢铁中是有害元素，使钢铁具有热脆性，虽然大部分硫在生铁冶炼中除去，但会增加熔剂的用量，引起渣量增加，铁产量减低，所以，要求铁矿石中硫的含量越低越好，一般要求应少于0.3%
目前，铁矿石中硫的标准分析方法有硫酸重量法和燃烧碘量法等.在低硫情况下，硫酸锁的沉淀不易完全：当硫含量高时，燃烧法热分解产生大量 SO.，滴定不易掌握.利用高频燃烧炉红外吸收法测定样品中的硫含量，为近代一些实验室所使用，此法方便快捷，精密度高，准确度好.目前我国尚未有此类分析方法的国家标准，为确保铁矿石中硫含量检测结果的准确性，广东省韶关钢铁集团有限公司
收稿日期：2010=06=02
（以下简称“韶钢”）对铁矿石中硫含量，特别是高硫试样采取硫酸钡重量法、XRF法和高频燃烧炉红外吸收法3种方法进行了比对.经过探索与实践，建立了高频燃烧炉红外吸收法测定铁矿石中硫含量的实验室内部检验方法，确保铁矿石中硫含量检测结果的准确性，检测范围覆盖韶钢日常铁矿石硫的检测范围。
1实验部分 1.1仪器
LECO公司CS-600红外碳硫分析仪，每次分
析样品前必须预热1h以上， 1.2试剂和材料
碱石棉、无水过氯酸镁、玻璃棉、脱脂棉、镀铂硅胶、稀土氧化铜均为分析纯.助熔剂：纯钨（w（S）<
作者简介：武映梅（1971-），女，1993年毕业于云南民族大学化学系，高级工程师。