·表面改性技术与工艺·
马氏体不锈钢表面低温渗碳层腐蚀行为研究
徐昂，刘瑞良
（哈尔滨工程大学材科学与化学工程学院，黑龙江哈尔滨150001）
摘要：本文采用低温等离子渗碳技术对431、15-5PH和17-4PH等马氏体不锈钢进行了不同温度下的改性处理，利用极化曲线和阻抗谱等方法研究了低温渗碳层的腐蚀行为。结果表明，15-5PH和 17-4PH不锈钢，随渗碳温度升高，渗碳层表面耐蚀性略有下降，而431不锈钢则相反；三种不锈钢表
面的低温渗碳层腐蚀机理相同，且不随温度发生改变。关键词：马氏体不锈钢；低温渗碳；极化曲线；阻抗谱
中图分类号：TG113.23+1文献标志码：A文章编号：1673-4971(2015)05-0031-06
StudyonCorrosionBehaviorofLowTemperatureCarburized
layer on Martensitic Stainless Steel Surface
XU Ang, LIU Rui-liang
(School of Materials Science and Chemical Engineering, Harbin Engineering University ,Harbin Heilongjiang 150001 , China)
Abstract: In the present paper, modification treatment of 431,15-5PH and 17-4PH etc.martensitic stain-less steels were conducted under different temperature by low temperature plasma carburizing. The corro-sion behavior of low temperature carburizing were studied by polarization curves and impedance spectrosco-py. The results show that the corrosion resistance of the carburized layer decreases slightly with tempera-ture increasing for 15-5PH and 17-4PH stainless steel, but 431 stainless steel is opposite. The corrosion mechanism of low temperature carburized layer on three kinds of stainless steel is the same, and do not change with temperature increasing.
Key words;martensitic stainless steel; low temperature carburizing; polarization curves; impedance spec-troscopy
不锈钢在使用环境中能自钝化而具有优良的耐腐蚀性，因此广泛应用于家用电器、纺织工业、汽车工业，以及化工设备、建筑、船舶等领域1。然而不锈钢在石油化工、电气电站以及船舶和海洋工程摩擦腐蚀环境下硬度和耐磨性受到严峻挑战。
表面改性处理是改善不锈钢表面性能的主要方法[}]。其中渗碳是化学热处理中重要的方法之一，一般在高温（930℃左右）下进行。在这-温度下，
收稿日期：2015-05-26
渗层中会产生有铬的碳化物析出，在显著提高表面硬度的同时，表面耐蚀性能却严重恶化，失去了不锈钢原有的特性。低温渗碳处理解决了这一问题[3]。但目前的研究主要集中在渗碳工艺的优化、渗层组织结构的表征以及渗层机械性能和摩擦性能测试等方面，关于不锈钢（特别是马氏体不锈钢）表面渗层腐蚀的研究较少(4-5)。
本研究以431、15-5PH和17-4PH马氏体不锈钢
作者简介：昂（1994.9-），男，本科，主要从事金属表面腐蚀行为方面研究。
联系电话：18604507402；E-mail;623722902@qq.com