第34卷第5期 2013年10月
热处理技术与装备
RECHULI JISHUYUZHUANGBEI
镧-铈混合稀土变质剂对铸态高速钢
组织与性能的影响
刘秋香，陆德平，陆磊，胡强，付青峰，周喆（江西省科学院江西省铜钨新材料重点实验室，江西南昌330029）
Vol.34,No.5 Oet,2013
·性能研究·
摘要：研究了鋼-铈稀土变质对铸态高速钢组织及性能的影响。试验表明经稀土变质处理后，高速钢铸态组织中共晶碳化物明显细化，鋼-铈混合稀土的添加促使共晶碳化物断网和团球化。此外，
-混合稀土的添加提高了高速钢的冲击韧性和抗弯强度，其强度分别提高了26%和7.8%。关键词：鋼-饰混合稀土；变质剂；高速钢；共晶碳化物
中图分类号：TG142.71文献标识码：A文章编号：1673-49712013)05-0049-04
EffectofMischmetalAterantonMicrostructureandMechanical
Properties of As-cast High-speed Steel
LIUQiu-xiang，LUDe-ping，LULeiHU Qiang，FUQing-feng，ZHOUZhe
(Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials, Jiangxi Academy of Sciences,
Nanchang Jiangxi 330029, China)
Abstract: The effects of mischmetal alterant on microstructure and mechanical properties of as-cast high speed steel were investigated. The results showed that the eutectic carbide in microstructure of as-cast seaeeaaeasa the meshy eutectic carbides were changed into spherical one, and the impact toughness and bending
strength of high-speed steel were increased by 26% and 7.8% respectively-Key words: mischmetal; alterant;high-speed steel;eutectic carbide
高速钢是一种广泛应用的工模具材料，具有优异的韧性、耐磨性和抗热疲劳性能11-2]。在装备工业快速发展的今天，高速钢的作用引起了人们更加广泛关注。众所周知，高速钢中含有大量碳化物形成元素，因此碳化物是高速钢中的一个重要组成相。高速钢中碳化物的数量、分布和形貌等是决定高速钢性能的重要因素，而合金元素以及热处理对碳化物有较为明显的影响[3-5]。人们就稀土对高速钢凝固组织的影响开展了一系列研究工作。研究结果表
收稿日期：2013-08-19
明，稀土元素对高速钢的凝固组织有明显细化作用，并且促进碳化物在加热时断网和球团化(7-8)，但是对-铺稀土的研究较少。本文就镧-铈稀土对铸态高速钢组织与性能的影响进行了研究。
1试验材料与方法 1.1试验材料
将废弃的M2高速钢棒，除油污一清洗一烘干之后，用25kg中频真空感应炉进行重熔，当温度达到
作者简介：刘秋香（1981-），女，博士，助理研究员，主要从事金属材料研究。
联系电话：079188177237;E-mail:q0813@126.com
基金项目：国家科技支撑计划课题（2011BAC10B04）万方数据